1. Two types: open type (K type) and closed type (F type)

2. Design pressure:   Padding seal:   0.2Mpa

                  Mechanical seal: 0.4Mpa

                  Jacket:        0.6Mpa

3. Design temperature: 0-200℃

4. Operating temperature: 0-180℃

5. High voltage test: 20kv

6. Glass-enamel layer thickness: 0.8-2.0MM

7. Capacity: 50 - 30,000L

8. Agitator: Anchor type, Turbine type, Paddle type, Combination type

9. Speed reducer: Vertical speed reducer

10. Shaft seals: Padding seal (0.2Mpa)

           Single surface mechanical seal (0.4Mpa)

           Double surface mechanical seal (0.6Mpa, 1.0Mpa)

11.Corrosion resistance: organic or inorganic acid, organic solution and weak alkaline corrosion (not including hydrofluoric acid, which the consistency of fluorine medium is more the 30%, phosphoric acid and alkali ,when consistency are more than 30% and temperature higher than or equal to 180℃.)

12. Resistance to sharp temperature variation: cool shock 110℃,hot shock 120℃

13. Temperature should be slowly changed while heating or cooling glass lined

14. If the design pressure of the tank surpasses 0.6Mpa, this kind of glass lined reactor needs specially to order.

Note: Above the information is only a part, our factory can produce glass lined chemical equipments in various types according to the customer's request.